SS01 should be stored at room temperature (23±2°C) in a retainer storage box for optimal preservation.
Splint Hard is an excellent option for printing rigid occlusal splints, offering optimal elongation, high flexural strength, and low water absorption. This material is TPO-free, tasteless, and free from MMA & THF-MA, making it a safer choice, especially for sensitive users.
SH01 has undergone real-aging performance testing in oral devices and features exceptional shrinkage control and high precision, ensuring long-term durability. With the HyperClear system, it provides outstanding transparency for occlusal splint applications. Additionally, printed splints require minimal polishing in supported areas.
For best storage, SS01 should be kept at room temperature (23±2°C) in a retainer storage box.
-TPO-free
-MMA & THF-MA free
-Minimal polish using HyperClear system
-Transparent, high flexural strength, optimum elongation
Physical Properties – Liquid Status
| Property | Value |
|---|---|
| Colour | Transparent |
| Viscosity | 1050 |
| Wavelength | 405nm |
Mechanical Properties – Post Cured Parts
| Property | Value | Test Method |
|---|---|---|
| Ultimate Flexural Strength | > 50 MPa | ISO 20795-2 |
| Flexural Modulus | > 1500 MPa | ISO 20795-3 |
| Elongation at Break | > 20% | ISO 527 |
| Fracture Work | > 6000 J/m² | ISO 20795-1 |
| Maximum Stress Intensity | > 3.9 MPa m1/2 | ISO 20795-1 |
| Maximum Stress Intensity after Three Months of Accelerated Aging Tests | > 3.9 MPa | ASTM F1980-2021, ISO 527 |
Post Processing
| Process | Value |
|---|---|
| Cleaning Time with 95% Ethanol | Manual Cleaning 20 secs |
| Recommended Curing Time | Fabcure 1/1S: 10 min | Fabcure 2: 5 min |