Dental equipment supplier in Canada
220.00$
Available on backorder
The Dental Model DM12 is an excellent option for printing segmented models used in crown and bridge applications. Compared to its predecessor, DM11, it offers enhanced precision due to its reduced elasticity and increased flexural modulus. The cured resin’s superior hardness and mechanical properties provide excellent resistance to abrasion during seating and finishing, ensuring a precise fit for crown and bridge cases. Its yellow color enhances visibility of margin lines and adjacent contours, while its low-viscosity formula allows for effortless cleanup.
| Property | Value | Test Method |
|---|---|---|
| Hardness | Shore D 81 | ISO 868 |
| Tensile Modulus | 1404 MPa | ISO 527 |
| Tensile Strength | 29 MPa | ISO 527 |
| Elongation at Break | 11% | ISO 527 |
| Flexural Modulus | 1537 MPa | ISO 178 |
| Flexural Strength | 52 MPa | ISO 178 |
Cleaning time with 95% ethanol: Manual cleaning: 30 + 30 secs
Recommended curing time: Fabcure 1: 10 mins, Fabcure 2: 7 mins
The Dental Model DM12 is an excellent option for printing segmented models used in crown and bridge applications. Compared to its predecessor, DM11, it offers enhanced precision due to its reduced elasticity and increased flexural modulus. The cured resin’s superior hardness and mechanical properties provide excellent resistance to abrasion during seating and finishing, ensuring a precise fit for crown and bridge cases. Its yellow color enhances visibility of margin lines and adjacent contours, while its low-viscosity formula allows for effortless cleanup.
| Property | Value | Test Method |
|---|---|---|
| Hardness | Shore D 81 | ISO 868 |
| Tensile Modulus | 1404 MPa | ISO 527 |
| Tensile Strength | 29 MPa | ISO 527 |
| Elongation at Break | 11% | ISO 527 |
| Flexural Modulus | 1537 MPa | ISO 178 |
| Flexural Strength | 52 MPa | ISO 178 |
Cleaning time with 95% ethanol: Manual cleaning: 30 + 30 secs
Recommended curing time: Fabcure 1: 10 mins, Fabcure 2: 7 mins