Dental Cast DC12 is a wax-like, 3D-printable photopolymer specifically designed for investment casting. It is an excellent choice for dental applications, including crown and bridge casting, as well as cast partial denture frameworks. DC12 ensures a clean burnout with minimal deformation and is also suitable for pressed ceramic applications.
| Property | Value |
|---|---|
| DC12 | Crown, Bridge, Partial Framework |
| Property | Value | Test Method |
|---|---|---|
| Color | Green | – |
| Viscosity @25℃ | cps | 128 | – |
| Wavelength | 405nm | – |
| Post Processing | ||
| Cleaning time with 95% ethanol | Ultrasonic bath: 60 + 10 secs | – |
| Recommended curing time | Fabcure 1: 4 mins, Fabcure 2: 3 mins | – |
| Hardness | Shore D | 83 | ISO 868 |
| Tensile Modulus | MPa | 1693 | ISO 527 |
| Tensile Strength | MPa | 40 | ISO 527 |
| Elongation at break | % | 2.8 | ISO 527 |
| Flexural Modulus | MPa | 1469 | ISO 178 |
| Flexural Strength | MPa | 20 | ISO 178 |
Dental Cast DC12 is a wax-like, 3D-printable photopolymer specifically designed for investment casting. It is an excellent choice for dental applications, including crown and bridge casting, as well as cast partial denture frameworks. DC12 ensures a clean burnout with minimal deformation and is also suitable for pressed ceramic applications.
| Property | Value |
|---|---|
| DC12 | Crown, Bridge, Partial Framework |
| Property | Value | Test Method |
|---|---|---|
| Color | Green | – |
| Viscosity @25℃ | cps | 128 | – |
| Wavelength | 405nm | – |
| Post Processing | ||
| Cleaning time with 95% ethanol | Ultrasonic bath: 60 + 10 secs | – |
| Recommended curing time | Fabcure 1: 4 mins, Fabcure 2: 3 mins | – |
| Hardness | Shore D | 83 | ISO 868 |
| Tensile Modulus | MPa | 1693 | ISO 527 |
| Tensile Strength | MPa | 40 | ISO 527 |
| Elongation at break | % | 2.8 | ISO 527 |
| Flexural Modulus | MPa | 1469 | ISO 178 |
| Flexural Strength | MPa | 20 | ISO 178 |